RubberBit KS-580 High polymer modified bitumen waterproof coating
- Implementation standards：
1.The material is a aquatic product, with non-toxic, no smell, non combustible characteristics, safe and reliable;
2.The material is a single component, cold method construction, simple operation;
3.Acid and alkali resistance,aging resistance, long service life;
4.The film has good flexibility, crack resistance and heat durability, good adhesion, is a kind of ideal waterproof material;
5.Good compatibility with other waterproof membrane, melting after re heating in the film state , the materials can be perfectly joint with the hot melt method constructed modified bitumen, to form a composite high grade waterproof structure.
WHERE TO USE
1.Non exposed waterproofing of roof and underground structures.
2.Compound with all kinds of modified bitumen waterproofing membrane to composite strong waterproof layer.
3.As basic treatment agent for all kinds of modified bitumen waterproof membrane.
4.Can be directly coated in a variety of pipe, concrete surface to function as protection, anti-corrosion effect.
DATA BASE IMPLEMENTED STANDARD: JC/T408-2005
|Solid content / % ≥||45|
|Heat resistance / ℃||80 ± 2||110 ± 2|
|No sliding. flowing, dripping|
|Impermeability 0.10Mpa.30min||0.10Mpa.30min No leakage|
|Adhesion strength / Mpa ≥||0.30|
|Surface drying time / h ≥||8|
|Actual drying time，h ≥||24|
|Low temperature flexibility / ℃||Standard condition||-15||0|
|Break elongation / % ≥||Standard condition||600|
|The buyer and the supplier can negotiate a lower low temperature index|